Stainless Properties
SPECIFICATION
Stainless Steel 200 Series | |||||||||||||
Grade | Chemical Composition | Mechanical Properties | |||||||||||
C | Si | Mn | P | S | Ni | Cr | N | Cu | Mechanical Properties | Y.S | T.S. | ELOG. | |
% | % | % | % | % | % | % | % | % | mm2 | mm2 | % | % | |
201 | ≦ 0.15 | ≦ 1.00 | 8~11 | ≦ 0.060 | ≦ 0.030 | 0.9~1.5 | 15~17 | ≦ 0.25 | 1.5~2 | ≧310 | ≧665 | ≧35 | ≧105 |
(1% Ni) | |||||||||||||
202 | ≦ 0.15 | ≦ 1.00 | 6~9 | ≦ 0.060 | ≦ 0.030 | 3.5~5 | 15~17 | ≦ 0.25 | 1.5~2 | ≧260 | ≧620 | ≧40 | ≧100 |
(4% Ni) | |||||||||||||
● The specification of type 201 and 202 according with Mill Standard. |
Stainless Steel 300 Series | |||||||||||||
Grade | Chemical Composition | Mechanical Properties | |||||||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Y.S | T.S. | ELOG. | HRB | ||
% | % | % | % | % | % | % | % | mm2 | mm2 | % | |||
304 | ≦ 0.08 | ≦ 0.75 | ≦ 2 | ≦ 0.045 | ≦ 0.03 | 8~10 | 18~20 | ≧205 | ≧520 | ≧40 | ≧90 | ||
301 | ≦ 0.15 | ≦ 1.00 | ≦ 2 | ≦ 0.045 | ≦ 0.03 | 6~8 | 16~18 | ≧205 | ≧515 | ≧40 | ≧95 | ||
316 | ≦ 0.08 | ≦ 1.00 | ≦ 2 | ≦ 0.045 | ≦ 0.03 | 10~14 | 16~18 | 2~3 | ≧205 | ≧515 | ≧40 | ≧90 | |
316L | ≦ 0.03 | ≦ 1.00 | ≦ 2 | ≦ 0.045 | ≦ 0.03 | 12~15 | 16~18 | 2~3 | ≧170 | ≧480 | ≧40 | ≧95 | |
● The specification of type 301, 304, 316, 316L according with ASTM and JIS standard. |
Stainless Steel 400 Series | |||||||||||||
Grade | Chemical Composition | Mechanical Properties | |||||||||||
C | Si | Mn | P | S | Ni | Cr | N | Cu | Y.S | T.S. | ELOG. | HRB | |
% | % | % | % | % | % | % | % | % | mm2 | mm2 | % | ||
430 | ≦ 0.12 | ≦ 1.00 | ≦ 1 | ≦ 0.040 | ≦ 0.030 | 16~18 | ≧205 | ≧450 | ≧22 | ≦88 | |||
● The specification of type 430 according with ASTM and JIS standard. |
Surface Treatment
Item | Surface finishing | Surface finishing methods | Main application |
NO.1 | HR | Heat treatment after hot rolling, pickling, or with treatment | For without the purpose of the surface gloss |
NO.2D | Without the SPM | Method of heat treatment after cold rolling, pickling surface roller with wool or eventually a light rolling a matte surface processing | General materials,building materials. |
NO.2B | After SPM | Giving No.2 processing materials appropriate method of cold light sheen | General materials, building materials ( most of the goods are processed ) |
BA | Bright annealed | Bright heat treatment after cold rolling , in order to be more shiny, cold light effect | Automotive parts, home appliances, vehicles, medical equipment, food equipment |
NO.3 | Shiny, coarse grain processing | The NO.2D or NO.2B processing timber No. 100-120 polishing abrasive grinding belt | Building materials, kitchen supplies |
NO.4 | After CPL | The NO.2D or NO.2B processing timber No. 150-180 polishing abrasive grinding belt | Building materials, kitchen supplies, vehicles, medicals |
240# | Grinding of fine lines | The NO.2D or NO.2B processing timber 240 polishing abrasive grinding belt | Kitchen appliances |
400# | Close to BA luster | The MO.2B timber 400 polishing wheel polishing method | Building materials, kitchen utensils |
HL(hair lines) | Polishing line having a long continuous processing | In a suitable size ( usually mostly No. 150-240 grit ) abrasive tape for as long as the hair, having a continuous processing method of polishing line | The most common building materials processing |
NO.6 | NO.4 processing less than the reflection , the extinction | NO.4 processing material used for polishing Tampico brushing | Building materials, decorative |
NO.8 | Highly accurate reflectance mirror processing | No. 600 of the rotary buff with a polishing | Building materials, decorati |